Jadual Sifat Seramik Lanjutan
Sifat-sifat Unit-unit Seramik oksida Seramik nitrida Seramik Karbida Seramik Lain
Alumina ZTA Zirkonia Oksida Berilium Nitrida Aluminium Silikon nitrida Boron nitrida Karbid Silikon Seramik yang boleh dikerjakan
96% 99.7% 99.95% ZTA 3YZ Magnesium-polivinil sulfonat Zirkonia Hitam BeO AL170 AL200 AL230 GPSN HPSN 99% Ketulenan (Kinerja Tinggi) Kekeklusan 99.51% Kekeklusan 99.81% Pirolitik (PBN) BN+AlN BN-B BN-C BN-D BN-S BN-S2 BN-S+ Karbur silikon terinter Karbon Silikon Berikatan Reaksi Macor MGC
Kekuatan mampatan Megapascal 2000 2000 3500 2500 2000 2000 2000 1700 2100 — — 3000 3000 120 120 120 154 ∥ / 550 ⊥ 110 130 225 220 380 420 480 2500 2500 345 450
Ketumpatan g/cm3 3.75 3.95 3.98 4.1 6.05 5.7 6.0 2.86 3.3 3.3 3.3 3.2 3.3 2.0 2.1 2.2 2.1-2.2 2.25-2.35 2.40-2.50 2.80-2.90 2.80-2.90 2.20-2.30 2.55-2.65 2.75-2.85 3.1 3.1 2.52 2.6
Kekuatan Lenturan @ 25°C Megapascal 200-300 250-350 500-600 600 1200 500 1000 200 400 400 400 700 900 30-40 45 50 80 ∥ / 173 ⊥ 65 85 115 120 150 220 320 410 400 94 110
Ketahanan retakan KIC MPa m1/2 4.5 4 4.5 7 8 8 8 2 3.0 3.0 3.0 6.0 7.0 2.6 ~3 ~3 — — — — — — — — 4.6 4.0 1.5 1.8
Kekerasan GPa 12 14 18 16 13.5 11 12 12 11 11 11 14 16 0.25 ~0.4 ~0.5 — — — — — — — — 28 20 2.3 2.5
Modulus Young GPa 300 370 400 335 200 200 200 300 330 330 330 280 310 40 45 50 25 ∥ / 90 ⊥ — — — — — — — 350-400 350 66.9 70
Konduktiviti terma @ 25°C W/m·K 25 33 45 20 2 2 2 200 170 200 230 20 30 32 35 40 2 ∥ / 60 ⊥ 30 30 20 80 40 40 40 102.6 150 1.5 1.6
CTE pada 25°C – 1000°C 10-6/K 6.3 6.5 7.5 7 10 9 10 8 4.6 4.6 4.6 3.0 2.8 2.5 2.6 2.8 1.0 ∥ / 4.5 ⊥ 2.0 2.8 3.5 2.8 2.7 2.7 2.7 4.02 4.5 9.0 9.2
Suhu Udara Maksimum darjah Celsius 1600 1700 1750 1500 800 800 800 1800 1200 1200 1200 1100 1200 850 900 900 900 1000 1000 1000 1000 1000 1000 1000 1200 1380 800 850
Suhu Maksimum (Iners) darjah Celsius 1600 1700 1750 1500 1000 1500 1500 2000 1350 1350 1350 1300 1400 2000 2000 2000 2100 1800 1800 1800 1800 1800 1800 1800 1900 1380 1000 1050
Pemalar dielektrik pada 1 MHz – 9.8 9.9 9.9 10 29 20 20 6.7 9.0 9.0 9.0 7.5 8.5 4-5 ~4 ~4 3.4 ∥ / 5.2 ⊥ — — — — — — — — 8.0 6 6.2
Ketahanan dielektrik (DC) kV/mm 9 11 16 16 18 10 18 40 >15 >15 >15 20 18 >40 >40 >40 >50 — — — — — — — — — 62 65
Rintangan isip @ 25°C ohm-sentimeter >1014 >1014 >1016 >1016 >1012 >1012 >1012 >1014 >1014 >1014 >1014 >1015 >1014 >1013 >1013 >1013 >1015 >1013 >1012 >1012 >1013 >1013 >1013 >1013 102–1011 102–103 >1017 >1017

Nota: Nilai sebenar mungkin berbeza mengikut kumpulan, bentuk dan saiz; oleh itu, data ini hanya untuk rujukan dan kami tidak memberikan sebarang jaminan.